Effect of microstructure and casting defects on the mechanical properties of secondary AlSi10MnMg(Fe) test parts manufactured by vacuum assisted high pressure die casting technology
Primary AlSi10MnMg alloy is widely used for manufacturing of high ductility VPDC castings. This alloy combines low Fe with high
Processing Thickness Window for As-cast Ausferritic Castings
A process to obtain ausferritic as-cast microstructures through engineered cooling after solidification (without heat treatment) was developed in previous studies
Advanced Properties of Ausferritic Ductile Iron Obtained in As-Cast Conditions
Ductile iron casting production is strongly affected by austenite and graphite distribution obtained after the solidification process. At the same
Understanding Superfine Graphite Iron Solidification Through Interrupted Solidification Experiments
The tensile strength of near-eutectic gray iron can be increased from 230–300 to 300–345MPa, without a significant increase in hardness,
Comportamiento frente a la corrosión de fundiciones con grafito laminar y esferoidal parcialmente modificadas con silicio en NaCl 0,03 M
El uso creciente de fundiciones esferoidales en aplicaciones tecnológicas hace que se busquen nuevos métodos para mejorar su comportamiento frente
Enhancing the stationary state prediction in Model Predictive Control systems to avoid Dross defect in heavy-section foundries
A Model Predictive Control (MPC) is a system designed to control a production plant. These systems are composed by several
Advanced sustainable foundry – Carbon balance and carbon footprint in foundry processes and foundry product cycles
Carbon footprint analysis (CFA) is a sophisticated environmental method to evaluate the impact of the whole life-cycle of a product
Austenite stability of austempered ductile iron (ADI) in sub-zero conditions
The use of Austempered Ductile Iron (ADI) in the manufacture of different types of components grows despite some limitations that
Fracture characterization of new generation ferritic spheroidal cast irons
Nearly all cast parts must undergo a machining process in order to be used in service. This work is exclusively
Improved precision in grain size prediction by thermal analysis and statistical analysis in aluminium castings
Primary AlSi10MnMg alloy is the most widely used alloy for manufacturing of vacuum assisted high pressure die castings (VPDC) with
Microstructural features of primary and secondary ductile high pressure die casting alloys for the automotive industry
Primary AlSi10MnMg alloy is the most widely used alloy for manufacturing of vacuum assisted high pressure die castings (VPDC) with
Effect of microalloying element addition on the microstructure, mechanical and corrosion behaviour of A356 secondary alloy with 0.30% Fe
This work investigated how trace additions of Mn, Cr and V affect the morphologies of harmful BETA-AlFe5Si intermetallics, mechanical properties
Effect of Carbon Equivalent and Alloying Elements on the Tensile Properties of Superfine Interdendritic Graphite Irons
Recently, it was demonstrated that the tensile strength of gray iron of average 4% Carbon Equivalent can be increased to
Kinetics of graphite expansion during eutectic solidification of cast iron
The paper introduces a new linear displacement analysis (LDA)/thermal analysis (TA) experimental device for measuring linear displacement during the solidification
Evolución del grafito y de la fracción sólida durante la solidificación de fundiciones nodulares
La producción de fundición de hierro dúctil se ve fuertemente afectada por la distribución de austenita y grafito obtenida después
As-cast high silicon ductile irons with optimised mechanical properties and remarkable fatigue properties
The present work shows a comparative study regarding the mechanical properties of 25 as cast ferritic ductile iron alloys, nine