Investigation on the Effect of Sulfur and Titanium on the Microstructure of Lamellar Graphite Iron
The goal of this work was to identify the inclusions in lamellar graphite cast iron in an effort
Waste From Metallurgic Industry: A Sustainable High-Temperature Thermal Energy Storage Material
The ambitious DOE SunShot cost target ($0.06/kWh) for concentrated solar power (CSP) requires innovative concepts in the collector,
Effect of the Thermal Modulus and Mould Type on the Grain Size of AlSi7Mg Alloy
Thermal analysis has been used for decades for melt control before casting aluminum alloys. However, obtaining a good
Redistribution and Effect of Various Elements on the Morphology of Primary Graphite in Cast Iron
It has been shown repeatedly that many elements present as traces or at low level can affect graphite
Supervised learning classification for dross prediction in ductile iron casting production
Foundry is one of the key axes in society because it provides with important pieces to other industries.
Gray cast iron with superfine graphite, high primary austenite fraction and optimized mechanical properties
The present invention describes a flake graphitic cast iron with a chemical composition which allows obtaining superfine graphite
Study of the Effect of Cooling Rate on Eutectic Modification in A356 Aluminium Alloys
In this present work, an assessment of eutectic modification based on thermal analysis was performed on modified A356
Statistical Analysis of the Influence of Some Trace elements on Chunky Graphite Formation in Heavy Section Nodular Iron Castings
To study the formation of chunky graphite (CHG) in heavy section castings, 68 nodular cast irons of both
Influence of 1 wt-% addition of Ni on structural and mechanical properties of ferritic ductile irons
Two sets of ductile irons with and without Ni additions containing various low Si contents have been prepared
Critical temperature range in standard and Ni-bearing spheroidal graphite cast irons
Describing the conditions for reaustenitization of spheroidal graphite cast irons is of interest for theirheat-treatment after casting, e.g.
Optimization of chemical bonded sand moulds for big size cast components. Reduction of manufacturing costs
The production of big size cast components to accomplish the demanding market requirements requires advanced design concepts, a
Gray Cast iron with high austenite to eutectic ratio. Part III. High strength, low hardness, high carbon equivalent gray iron with superfine graphite
The standard methods to increase the mechanical properties of gray cast iron include the use of a lower
Gray cast iron with high austenite-to eutectic ratio. Part II. Increasing the austenite-to eutectic ratio trough inoculation
A higher amount of primary austenite in the microstructure of gray iron typically results in higher strength, if
Gray cast iron with high austenite to eutectic ratio. Part I. Calculation and experimental evaluation of the fraction of primary austenite in cast iron
The amount of primary austenite at the end of solidification in the microstructure of cast iron has a
Influence of wt.% addition of Ni on the structural and mechanical properties of ferritic ductile irons
Two sets of ductile irons with and without Ni additions containing various low Si contents have been prepared
Experimental evidence of metallurgical modification associated to chunky graphite in heavy section ductile iron castings
Heavy-section castings made of spheroidal graphite cast irons are known to be prone to graphite degeneracy. Upon the