The effect of heat treatment on gas porosity and mechanical properties was investigated in a step test part manufactured by vacuum assisted high pressure die casting using a new AlSi10MnMg(Fe) secondary alloy. Porosity and mechanical properties were investigated in the T6 temper with different solution heat treatments. Porosity was characterized by metallographic and fractographic analysis of the tensile specimens. Mechanical properties comparable to the corresponding primary alloy have been achieved for each solution heat treatment. It was found that increasing the solution temperature and time increased the yield and ultimate tensile strength, while elongation decreased and porosity observed on the metallographic sections and fracture surfaces increased. Porosity evaluation on the fracture surfaces indicates that the local area fraction rather than the one observed on the whole fracture surface determines ductility. The size of the largest pore appears to become more relevant above values of 200 µm.
Andrea Niklas, Sergio Orden, Asier Bakedano, M. da Silva, E. Nogués (Fundació Eurecat), Ana Isabel Fernández Calvo
Porositatea, presio-galdaketa, aluminio-aleazio sekundarioak, irudi-analisia, tratamendu termikoa, karakterizazio mekanikoa
Nola lagun diezazukegu?
Mantente informad@ de la actividad de AZTERLAN
Mantendu AZTERLANeko berrien adi
Manten zaitez AZTERLANeko informazioez eguneratuta