Thermal analysis has been used for decades for melt control before casting aluminum alloys. However, obtaining a good grain refinement in a standard cup does not ensure that the grain refinement is correct in real parts which may solidify at very different cooling rates. For this study, the effect of cooling rate on AlSi7Mg alloy with different metal qualities in terms of grain refinement was tested. The correlation between grain sizes measured on the standard cup with those obtained in cylindrical test parts with various diameters cast in sand and metallic moulds has been investigated. It was found possible to set up a formula for the grain size of the cylindrical test parts in function of their modulus and of the grain refinement obtained on the standard thermal cups. Corrective actions can then be taken in order to improve the metallurgical quality before casting.
Ibon Lizarralde, Anrea Niklas, Ana Isabel Fernández Calvo, Jacques Lacaze (CIRIMAT)
metales ligeros, aleaciones de aluminio, reducción de aluminio, fundición, tecnología de electrodos, refinador de grano, módulo térmico, solidificación, fundición de aluminio
¿Cómo podemos ayudarte?
Mantente informad@ de la actividad de AZTERLAN
Mantente informad@ de la actividad de AZTERLAN
Formamos equipos de trabajo en distintos ámbitos de la metalurgia y los procesos de transformación de metales.
Indícanos los datos de tu trabajo y nos pondremos en contacto contigo lo antes posible.
Comparte tu reto con nuestro equipo. Hablar no puede más que acercarnos un poco más a posibles soluciones.