10/2022
11th International Foundry Congress (Turkey)
B+G+i, Burdin-galdaketa, Galda teknologiak, Rodolfo González-Martínez, Susana Méndez, Urko de la Torre
The ADI family shows the best resistance ductility relationship of the ductile iron materials due to an ausferritic microstructure. This research work is focused on the as-cast state obtention of this type of microstructures, with no need of heat treatment. It studies the effect of section size and holding time on the evolution of the microstructure and mechanical properties of as-cast ausferritic ductile iron.
For that, Y block standard samples of 50.0 mm thickness and thermal analysis cups were produced using a novel engineered cooling methodology. The temperature arrest was performed at 400ºC and the hoplding time changed from 0 to 180 minutes. The obtained experimental results show that 60 minutes holding time are needed to obtain the optimal mechanical properties (U.T.S>800MPa and El.>12%).
Urko de la Torre, Rodolfo González-Martínez, Susana Méndez.
ADI, as-cast, ausferrite, controlled cooling, egineered cooling.
Nola lagun diezazukegu?
Mantente informad@ de la actividad de AZTERLAN
Mantendu AZTERLANeko berrien adi
Manten zaitez AZTERLANeko informazioez eguneratuta